| About |
|---|
| Jet Black General Grade CHARACTERISTICS: Jet black, High gloss&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 2.40 | g/10min | ASTM D1238 |
| 220℃，10.0kg | 24.00 | g/10min | ASTM D1238 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 96 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 86 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| 102 | ℃ | ASTM D1525 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50mm | HB | UL-94 | |
| 3.00mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃ | 150 | J/m | ASTM D256 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 110 | R 级 | ASTM D785 |
| tensile strength | |||
| 23℃ | 46.1 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | |||
| bending strength | |||
| 23℃ | 77.5 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 2650 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion molding conditions | Nominal value | Unit | Test method |
| Drying temperature | 70 -80 | °C | |
| Drying time | 2.0-3.0 | Hr | |
| Injection temperature | |||
| Mold temperature | 40-80 | °C | |
| Drying temperature | 70-80 | °C | |
| Drying time | 2.0-3.0 | Hr | |
| Die temperature | 190-230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 80°C/8hr |
| 3. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |