| Heat Resistant Grade CHARACTERISTICS: Super high heat&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 4.5 | g/10min | ISO 1133 |
| 220℃，10.0kg | 4.5 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.70 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，6.4mm | 140 | J/m | ISO 180 |
| 23℃，6.4mm | 140 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 116 | ℃ | ASTM D648 |
| 1.8 MPa, annealed | 116 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed, 12.7 mm | 106 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed, 12.7 mm | 106 | ℃ | ASTM D648 |
| Vicat Softening Temp | 125 | ℃ | ASTM D1525 4 |
| Vicat Softening Temp | 125 | ℃ | ISO 306/A |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.50 mm, all colors | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 39.0 | MPa | ISO 527-2 |
| 23℃ | 39.2 | MPa | ASTM D638 |
| Bending modulus | |||
| 23℃ | 2350 | MPa | ASTM D790 |
| 23℃ | 2350 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 69.0 | MPa | ASTM D790 |
| 23℃ | 69.0 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 107 | ISO 2039-2 | |
| R-level | 107 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 95 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Mold temperature | 40 to 90 | °C | |
| Injection pressure | 68.6 to 118 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 80°C/8hr |
| 3. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |