| About |
|---|
| TAIRILAC® WE810P is an Acrylonitrile Styrene Acrylate (ASA) product. It can be processed by extrusion and is available in Asia Pacific, Europe, or North America. Primary characteristic: reach compliant.&& |
| Product Description | |
|---|---|
| Generic | ASA |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.08 | g/cm³ | ASTM D792 |
| 23℃ | 1.08 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 8.0 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 160 | J/m | |
| 23℃，6.4mm | 130 | J/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 12.7 mm | 77.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 90.0 | ℃ | ISO 306/A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 100 | ASTM D785 | |
| R-level | 100 | ISO 2039-2 | |
| tensile strength | |||
| 23℃ | 39.0 | MPa | ASTM D638 |
| Bending modulus | |||
| 23℃ | 2060 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 65.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 to 85 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Melt temperature | 180 to 220 | °C | |
| Nozzle temperature | 190 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |