| About |
|---|
| Transparent flame retardant grade CHARACTERISTICS: Transparent flame retardant sheet, transparent flame retardant injection parts. Transparency, Middle-low flow ability, UV stabilization, Flame retardant, Cl, Br, SB free.&& |
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Halogen free,Flame Characteristics,No antimony,Moderate liquidity |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.20 | g/cm³ | ASTM D792 |
| 23℃ | 1.20 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 9.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | ASTM D955 |
| 3.2 mm | 0.50 to 0.70 | % | ISO 2577 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 760 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 128 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 2.50 mm, all colors | V-0 | ||
| 3.00 mm, all colors | V-0 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 2500 µm | > 88.0 | % | ASTM D1003 |
| Haze | |||
| 2500 µm | < 2.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 122 | ASTM D785 | |
| R-level | 122 | ISO 2039-2 | |
| tensile strength | |||
| 23℃ | 64.0 | MPa | ASTM D638 |
| Bending modulus | |||
| 23℃ | 2160 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 103 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |