| About |
|---|
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Negative |
| Features | Good Hardness,Solvent resistance,Flame Characteristics |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile stress | |||
| fracture | 190 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 1.8 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| 23℃ | 1400 | MPa | ISO 178 |
| Bending stress | |||
| 23℃ | 280 | MPa | ISO 178 |
| Rockwell hardness | |||
| M scale | 100 | ISO 2039-2 | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 10 | KJ/m² | ISO 180/1A |
| Charpy Notched Impact Strength | |||
| 23℃ | 9 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 48 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 270 | ℃ | ISO 75-2/A |
| 8 MPa, unannealed | 200 | ℃ | ISO 75-2/A |
| Glass transition temperature | 90.0 | ℃ | ISO 11357-2 |
| Melting temperature | 280 | ℃ | ISO 11357-3 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.65 | ASTM D1183 | |
| Shrinkage rate | |||
| transverse | 0.4-0.6 | % | ISO 294-4 |
| ordinary | 0.2-0.6 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.02 | % | ISO 62 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant grade, File No. E162823 | |||
| 0.75mm | V-1 | UL 94 | |
| 1.5mm | V-0 | UL 94 | |
| 3.0mm | V-0，5VA | UL 94 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |