| About |
|---|
| General Purpose Grade CHARACTERISTICS: Metal plating&& |
| Product Description | |
|---|---|
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Europe,Asia Pacific,North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ASTM D792 |
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 240℃，5.0kg | 9.0 | g/10min | ASTM D1238 |
| 240℃，5.0kg | 9.0 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.60 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 490 | J/m | ISO 180 |
| 23℃，3.2mm | 490 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.35 mm | 92.0 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed, 6.35 mm | 92.0 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.50 mm, all colors | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 49.0 | MPa | ISO 527-2 |
| 23℃ | 49.0 | MPa | ASTM D638 |
| Bending modulus | |||
| 23℃ | 2550 | MPa | ISO 178 |
| 23℃ | 2550 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 81.0 | MPa | ISO 178 |
| 23℃ | 81.0 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 110 | ASTM D785 | |
| R-level | 110 | ISO 2039-2 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 95 to 105 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Temperature at the rear of the barrel | 210 to 240 | °C | |
| Temperature in the middle of the barrel | 230 to 260 | °C | |
| Front temperature of material barrel | 230 to 260 | °C | |
| Processing (melt) temperature | 240 to 260 | °C | |
| Mold temperature | 70 to 90 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |