| About |
|---|
| General Purpose Grade CHARACTERISTICS: Heat resistant&& |
| Product Description | |
|---|---|
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific,North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.14 | g/cm³ | ASTM D792 |
| 23℃ | 1.14 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 240℃，5.0kg | 7.5 | g/10min | ASTM D1238，ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.60 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃，3.2 mm | 570 | J/m | ISO 180, ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.35 mm | 103 | ℃ | ASTM D648，ISO 75-2/A |
| Vicat Softening Temp | 132 | ℃ | ISO 306/A, ASTM D1525 1 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 110 | ASTM D785 | |
| R-level | 110 | ISO 2039-2 | |
| tensile strength | |||
| 23℃ | 52.0 | MPa | ASTM D638, ISO 527-2 |
| Bending modulus | |||
| 23℃ | 2450 | MPa | ASTM D790, ISO 178 |
| bending strength | |||
| 23℃ | 89.0 | MPa | ASTM D790，ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 100 to 110 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 60.0 to 80.0 | °C | |
| Temperature at the rear of the barrel | 220 to 250 | °C | |
| Temperature in the middle of the barrel | 240 to 270 | °C | |
| Front temperature of material barrel | 240 to 270 | °C | |
| Processing (melt) temperature | 250 to 270 | °C | |
| Mold temperature | 70.0 to 90.0 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |