| About |
|---|
| Product Description | |
|---|---|
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific,Europe,North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：2.0 mm | 0.40 | % | ASTM D995 |
| Melt Flow Rate | |||
| 240℃，5.0kg | 18 | g/10min | ASTM D1238 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 92 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.20mm | V-0 | UL 94 | |
| 2.00mm | V-0，5VB | UL 94 | |
| 3.00mm | V-0，5VA | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃ | 59 | J/m | ASTM D256 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 117 | R 级 | ASTM D785 |
| tensile strength | |||
| 23℃ | 62.8 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | |||
| bending strength | |||
| 23℃ | 111 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 4020 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 100 -110 | °C | |
| Drying time | 3.0-4.0 | Hr | |
| Moisture content | 0.02 | % | |
| Injection temperature | |||
| Temperature at the rear of the screw barrel | 220-250 | °C | |
| Temperature in the middle of the screw barrel | 240-270 | °C | |
| Front temperature of screw barrel | 240-270 | °C | |
| Mold head temperature | 240-270 | °C | |
| Mold temperature | 70-90 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |