| About |
|---|
| Product Description | |
|---|---|
| Generic | PC+ABS |
| Material Status | Commercial: Negative |
| Features | Flame Characteristics |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| 23℃ | 1.18 | g/cm³ | ASTM D792 |
| Moulding shrinkage | |||
| Material flow direction | 0.4-0.7 | % | ASTM D955 |
| Melt Flow Rate | |||
| 240℃，5kg | 25 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 50mm/min | 640 | kg/cm² | ASTM D638 |
| elongation at break | |||
| 50mm/min | 120 | % | ASTM D638 |
| bending strength | |||
| 15mm/min | 1100 | kg/cm² | ASTM D790 |
| Bending modulus | |||
| 15mm/min | 28000 | kg/cm² | ASTM D790 |
| Rockwell hardness | |||
| 23℃ | 120 | R Scale | ASTM D785 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 1/8”，23℃ | 600 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.82MPa, 1/4 “, non annealed | 89 | ℃ | ASTM D648 |
| vicat softening point | |||
| 50N, 50 ℃/h, without annealing | 99 | ℃ | ASTM D1525 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.6mm, vertical combustion | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 90-100 | ℃ | |
| Drying time | 3-4 | h | |
| Maximum moisture content | 0.02 | % | |
| Melting temperature | 220-250 | ℃ | |
| Temperature at the rear of the barrel | 210-250 | ℃ | |
| Temperature in the middle of the barrel | 230-255 | ℃ | |
| Front temperature of material barrel | 235-260 | ℃ | |
| Nozzle temperature | 225-255 | ℃ | |
| Mold temperature | 80-90 | ℃ | |
| Back pressure | 5-15 | kg/cm² | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |