| About |
|---|
| General Purpose PS CHARACTERISTICS: High flow&& |
| Product Description | |
|---|---|
| Generic | PS (GPPS) |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.04 | g/cm³ | ASTM D792 |
| 23℃ | 1.04 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 10 | g/10min | ASTM D1238，ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 39.2 | MPa | ASTM D638 |
| 23℃ | 39.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.0 | % | ASTM D638 , ISO 527-2 |
| Bending modulus | |||
| 23℃ | 3240 | MPa | ASTM D790 , ISO 178 |
| bending strength | |||
| 23℃ | 74.0 | MPa | ASTM D790 , ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃，6.4 mm | 16 | J/m | ASTM D256 , ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed, 3.18 mm | 82.0 | ℃ | ASTM D648，ISO 75-2/A |
| Vicat Softening Temp | 93.0 | ℃ | ASTM D1525 , ISO 306/B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.50 mm, natural color | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Residual monomer | < 700 | ppm |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 75 | °C | |
| Drying time | 1.0 to 2.0 | hr | |
| Hopper temperature | 40 | °C | |
| Barrel rear temperature | 170 | °C | |
| Barrel middle temperature | 185 | °C | |
| Barrel front temperature | 200 | °C | |
| Nozzle temperature | 195 | °C | |
| Processing (melt) temperature | 160 to 210 | °C | |
| Mold temperature | 20 to 70 | °C | |
| Injection speed | 中等 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 80°C/2hr |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |