| High Impact PS CHARACTERISTICS: High flow, High impact, normal flow&& |
| Product Description | |
|---|---|
| Generic | PS (HIPS) |
| Material Status | Commercial: Active |
| Features | High impact resistance,High liquidity |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 200℃，5.0kg | 9.5 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 2160 | MPa | ASTM D638 |
| tensile strength | |||
| 23℃ | 23.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 40 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 2260 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 43.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，6.4mm | 110 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed, 3.18 mm | 90.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 97.0 | ℃ | ASTM D1525 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.50 mm, natural color | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Residual monomer | < 700 | ppm |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 75 | °C | |
| Drying time | 1.0 to 2.0 | hr | |
| Hopper temperature | 40 | °C | |
| Barrel rear temperature | 190 | °C | |
| Barrel middle temperature | 200 to 210 | °C | |
| Barrel front temperature | 205 | °C | |
| Processing (melt) temperature | 180 to 220 | °C | |
| Mold temperature | 20 to 70 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 80°C/2hr |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |