| Product Description | |
|---|---|
| Generic | SAN |
| Material Status | Commercial: Active |
| Features | High liquidity |
| Availabilitys | Europe,North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.07 | g/cm³ | ASTM D792 |
| Density | 1.07 | g/cm³ | ISO 1183 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，6.4mm | 17 | J/m | ISO 180 |
| 23℃，6.4mm | 17 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 12.7 mm | 90.0 | ℃ | ASTM D648 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 2.6 | g/10min | ASTM D1238 |
| 220℃，10.0kg | 26 | g/10min | ISO 1133 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.50 mm, all colors | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 71.0 | MPa | ISO 527-2 |
| 23℃ | 72.0 | MPa | ASTM D638 |
| Bending modulus | |||
| 23℃ | 3430 | MPa | ISO 178 |
| 23℃ | 3430 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 96 | MPa | ASTM D790 |
| 23℃ | 94 | MPa | ISO 178 |
| Rockwell hardness | |||
| M-level | 78 | ASTM D785 | |
| M-level | 78 | ISO 2039-2 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Barrel temperature | 210 to 250 | °C | |
| Nozzle temperature | 210 to 250 | °C | |
| Mold temperature | 50-70 | °C | |
| Injection pressure | 700-1250 | kg/cm² | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |