| TAISOX 2125是一种线性低密度聚乙烯材料,。 该产品在亚太地区、北美洲或欧洲有供货,加工方式为:流延薄膜。 TAISOX 2125的主要特性为:耐穿刺。 典型应用领域包括: 包裹物 电影&& |
| Product Description | |
|---|---|
| Supplier | fpc-tw |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good dissection,Low density,Puncture Resistant |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 20 | µm | |
| Secant modulus | ASTM D882 | ||
| 1% secant, MD: 20 µ m, cast thin film | 177 | MPa | ASTM D882 |
| 1% secant, TD: 20 µ m, cast thin film | 167 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 20 µ m, blow molded film | 9.81 | MPa | ASTM D882 |
| TD, yield, 20 µ m, blow molded film | 10.8 | MPa | ASTM D882 |
| MD, fracture, 20 µ m, blow molded film | 32.4 | MPa | ASTM D882 |
| TD, fracture, 20 µ m, blow molded film | 24.5 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 20 µ m, extruded film | 540 | % | ASTM D882 |
| TD, fracture, 20 µ m, extruded film | 710 | % | ASTM D882 |
| Drop hammer impact | |||
| 20 µ m, cast thin film | 150 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD: 20 µ m, cast thin film | 210 | g | ASTM D1922 |
| TD: 20 µ m, cast thin film | 460 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -70.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 93.0 | ℃ | ASTM D1525 |
| Melting temperature | 121 | ℃ |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 20 µ m, cast thin film | 96 | ASTM D2457 | |
| transparency | 95.0 | ASTM D1746 | |
| Haze | |||
| 20.0 µ m, cast thin film | 3.0 | % | ASTM D1003 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |