| About |
|---|
| TAISOX® 6630M is a Low Density Polyethylene material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of TAISOX® 6630M are: High Flow High Gloss Rigid Typical applications include: Consumer Goods Engineering/Industrial Parts Household Applications&& |
| Product Description | |
|---|---|
| Supplier | fpc-tw |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good wear resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 20 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | 50.0 | hr | ASTM D1693 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -60.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 92.0 | ℃ | ASTM D1525 |
| Melting temperature | 108 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 50 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| yield | 11.8 | MPa | ASTM D638 |
| fracture | 8.83 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 400 | % | ASTM D638 |
| Bending modulus | 177 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 150 to 180 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |