| About |
|---|
| TAISU PA6 T306HB 50GF是50％玻璃纤维增强的聚酰胺6树脂。它具有优异的机械性能和电气性能。 |
| Product Description | |
|---|---|
| Supplier | Taisu |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Electrical Properties |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.58 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.70 | % | |
| MD | 0.10 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 16000 | MPa | ISO 527-2 |
| Tensile stress (fracture) | 230 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.2 | % | ISO 527-2 |
| Bending modulus | 15000 | MPa | ISO 178 |
| Bending stress | 400 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 21 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 100 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 212 | ℃ | ISO 75-2/A |
| Melting temperature | 219 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 1.5E-5 | 1/℃ | |
| TD | 1.0E-4 | 1/℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level (1.6 mm) | HB | IEC 60695-11-10, -20 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Mold temperature | 100 | °C | |
| Ejection Temperature | 270 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |