| About |
|---|
| Taitacell EPS 391MM is an Expanded Polystyrene material. It is available in Asia Pacific or North America. Primary attribute of Taitacell EPS 391MM: Fast Molding Cycle. Typical applications include: Packaging Wire & Cable&& |
| Product Description | |
|---|---|
| Supplier | Taita |
| Generic | PS (EPS) |
| Material Status | Commercial: Active |
| Features | Quick molding cycle |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.0120 to 0.0250 | g/cm³ | ASTM D792 |
| water content | < 0.50 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| bending strength | > 0.196 | MPa | ASTM D790 |
| compressive strength | |||
| 10% strain | > 0.0686 | MPa | ASTM D695 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Thermal conductivity coefficient | 0.033 to 0.045 | W/m/K | ASTM C177 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Bead diameter | 1.20 to 1.80 | mm | |
| Chemical Resistance | |||
| Acid | Good | ||
| Alkali | Good | ||
| Solvent | Poor | ||
| Expandability | 70.0 to 85.0 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 95% min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |