| About |
|---|
| Taitalac® 8540T是一种丙烯腈丁二烯苯乙烯(ABS)材料,。 该产品在北美洲或亚太地区有供货,加工方式为:注射成型。 Taitalac® 8540T的主要特性有: 阻燃/额定火焰 Flame Retardant 高流动性 耐冲击 典型应用领域包括: 电气/电子应用 电气用具 电影 商业/办公用品&& |
| Product Description | |
|---|---|
| Supplier | Taita |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High liquidity,Flame Characteristics,V-0,5VA |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 200℃，5.0kg | 5.0 | g/10min | |
| 220℃，10.0kg | 45 | g/10min | |
| Shrinkage rate | |||
| MD | < 0.40 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | < 0.30 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 23℃，3.2mm | 190 | J/m | |
| 23℃，6.4mm | 170 | J/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 12.7 mm | 77.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 94.0 | ℃ | ASTM D1525 5 |
| Relative temperature index | |||
| Electrical performance, 1.57 mm | 60.0 | ℃ | UL 746 |
| Impact mechanical performance, 1.57 mm | 60.0 | ℃ | UL 746 |
| 1.57 mm | 60.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| High Arc Burning Index (HAI) (1.57 mm) | 10.0 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | 107 | mm/min | UL 746 |
| Hot wire ignition (HWI) (1.57 mm) | 57 | sec | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.59 mm | V-0 | ||
| 3.20 mm | 5VA |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 102 | ASTM D785 | |
| tensile strength | ASTM D638 | ||
| Yield, 23 ℃, 3.18 mm | 37.2 | MPa | |
| Fracture, 23 ℃, 3.18 mm | 29.6 | MPa | |
| Tensile strain | |||
| Fracture, 23 ℃, 3.18 mm | 20 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 2140 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 23 ℃ | 58.6 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 70.0 to 75.0 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 170 to 200 | °C | |
| Barrel middle temperature | 180 to 210 | °C | |
| Barrel front temperature | 170 to 200 | °C | |
| Nozzle temperature | 190 to 220 | °C | |
| Processing (melt) temperature | 165 to 175 | °C | |
| Mold temperature | 40.0 to 70.0 | °C | |
| Injection speed | 慢to中等 | ||
| Back pressure | 0.345 to 0.483 | MPa | |
| Screw speed | 30 to 100 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |