| Talcoprene® OC3030 CM GRIGIO313 is a Polypropylene material. It is available in Europe, Latin America, or North America for injection molding. Important attributes of Talcoprene® OC3030 CM GRIGIO313 are: Flame Rated REACH Compliant Typical application of Talcoprene® OC3030 CM GRIGIO313: Appliances&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | North America,Latin America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 25 | g/10min | ASTM D1238 |
| Shrinkage rate | 1.1 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 27.0 | MPa | ASTM D638 |
| Bending modulus | 2800 | MPa | ASTM D790 |
| bending strength | 48.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 28 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 66.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 92.0 | ℃ | ASTM D1525 3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 | hr | |
| Barrel rear temperature | 190 | °C | |
| Barrel middle temperature | 210 | °C | |
| Barrel front temperature | 230 | °C | |
| Mold temperature | 50 to 70 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |