| About |
|---|
| Product Description | |
|---|---|
| Supplier | Idemitsu |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Shrinkage rate | 0.5 ~ 0.7 | % | ASTM D955 |
| Density | 1.200 | g/cm³ | ISO 1183 B |
| Melt Flow Rate | |||
| 300℃，1.20kg | 8 | g/10min | ISO 1133 |
| Water absorption rate | |||
| 23℃，24hr，60% RH | 0.23 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 65 | MPa | ISO 527 |
| yield | 65 | MPa | ISO 527 |
| Nominal tensile fracture strain | 90 | % | ISO 527 |
| Tensile modulus | 2.000 | Mpa | ISO 527 |
| bending strength | 90 | MPa | ISO 178 |
| Bending modulus | 2.300 | MPa | ISO 178 |
| Rockwell hardness | 120/50 | R/M 级 | ISO 2039 |
| Taber abraser | 12 | mg (1000 rounds) | ASTM D1044 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 145 | ℃ | ISO 306 |
| Hot deformation temperature | |||
| 1.8 MPa | 125 | ℃ | ISO 75 |
| 0.45 MPa | 137 | ℃ | ISO 75 |
| Linear coefficient of thermal expansion | 6.5 | x 10 -5 cm/cm/ºC | ASTM D 696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | 2.85 | 106 Hz | IEC 60250 |
| 2.91 | 60 Hz | ||
| Dissipation factor | 0.0092 | 106 Hz | |
| 6.6 x 10 -4 | 60 Hz | ||
| Dielectric strength | |||
| 1.6 mm | 30E+5 | kV/mm | IEC 60243-1 |
| Arc resistance | 110 | sec | ASTM D495 |
| Volume resistivity | >10 16 | ohms·cm | IEC 60093 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | |||
| 87 | % | ISO 13468 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-2 | 0.36 ~ 1.90mm | UL 94 |
| HB | > 1.9 mm | File No. E48268 (M) | |
| Extreme oxygen index | 27 | % | ASTM D2863 |
| Hot wire ignition 1.47 mm | 3 | UL | |
| Igniting temperature of the hot wire | |||
| 2 mm | 850 | ℃ | IEC 60695-2-13 |
| Igniting temperature of the hot wire | |||
| 3 mm | 850 | ℃ | IEC 60695-2-13 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 80 | kJ/m² | ISO 179-1 EA |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Melt temperature | 280 ~ 305 | °C | |
| Mold temperature | 80 ~ 120 | °C | |
| Pre-drying | 4 hours/120°C | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |