| About |
|---|
| Transparency, Flame retardant&& |
| Product Description | |
|---|---|
| Supplier | Idemitsu |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-0 |
| Availabilitys | Africa & Middle East ,North America,Europe,Asia Pacific,Latin America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 5.00 | cm³/10min | ISO 1133 |
| Spiral flow length | 48.0 | cm | Internal Method |
| Molding shrinkage | Internal Method | ||
| TD：2.0 mm | 0.50 to 0.70 | % | Internal Method |
| MD：2.0 mm | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | |||
| Equilibrium, 23 ℃, 50% RH | 0.23 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 65 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed | 125 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 140 | ℃ | ISO 75-2/B |
| Coeff. of linear thermal expansion | |||
| MD | 6.5E-5 | 1/℃ | ISO 11359-2 |
| Relative Temperature Index (RTI) | |||
| Electrical performance | 80.0 | ℃ | UL 746 |
| Strength mechanical performance | 80.0 | ℃ | UL 746 |
| Impact mechanical performance | 80.0 | ℃ | UL 746 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric Strength | 30 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 MHz | 2.85 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 1.50 mm | V-0 | UL 94 |
| OPTICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Light Transmission | 85.0 to 89.0 | % | ISO 13468-1 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | >PC< |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | |||
| yield | 65.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| fracture | 70 | % | ISO 527-2 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Strength | 90.0 | MPa | ISO 178 |
| Rockwell hardness | ISO 2039-2 | ||
| M-level | 50 | ISO 2039-2 | |
| R-level | 120 | ISO 2039-2 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 120 | °C | |
| Drying Time | 5.0 to 8.0 | hr | |
| Rear Temperature Zone 1 | 260 to 300 | °C | |
| Middle Temperature Zone 2 | 260 to 300 | °C | |
| Front Temperature Zone 3 | 260 to 300 | °C | |
| Mold Temperature | 80 to 120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Mold Temperature: 104°F, Melt Temperature: 572°F, Injection Pressure: 1.81E+4 psi |
| 3. Thickness: 2mm / Width: 10mm |
| 4. 24h |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |