| About |
|---|
| Flame retardant&& |
| Product Description | |
|---|---|
| Supplier | Idemitsu |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-2,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 12.0 | cm³/10min | ISO 1133 |
| Spiral flow length | 25.0 | cm | Internal Method |
| Shrinkage rate | Internal Method | ||
| TD：2.0 mm | 0.50 to 0.70 | % | |
| MD：2.0 mm | 0.50 to 0.70 | % | |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.23 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 80 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 138 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 125 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | |||
| MD | 6.5E-5 | 1/℃ | ISO 11359-2 |
| Relative temperature index | |||
| Electrical performance, 1.20 mm | 130 | ℃ | UL 746 |
| Impact mechanical performance, 1.20 mm | 125 | ℃ | UL 746 |
| 1.20 mm | 130 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 30 | kV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 1 MHz | 2.85 | IEC 60250 | |
| Compared to the leakage tracing index | PLC 2 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.40 mm | V-2 | ||
| 1.20 mm | V-0 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | >PC |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | ||
| M-level | 50 | ||
| R-level | 120 | ||
| tensile strength | |||
| yield | 65.0 | MPa | ISO 527-2 |
| Nominal tensile fracture strain | 95 | % | ISO 527-2 |
| Bending modulus | 2300 | MPa | ISO 178 |
| bending strength | 90.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 5.0 to 8.0 | hr | |
| Barrel rear temperature | 260 to 300 | °C | |
| Barrel middle temperature | 260 to 300 | °C | |
| Barrel front temperature | 260 to 300 | °C | |
| Mold temperature | 80.0 to 120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Mold Temperature: 176°F, Melt Temperature: 572°F, Injection Pressure: 1.81E+4 psi |
| 3. Thickness: 2mm / Width: 10mm |
| 4. 24h |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |