| About |
|---|
| Product Description | |
|---|---|
| Supplier | Idemitsu |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High liquidity |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Shrinkage rate | |||
| MD：1.6 mm | 0.5 ~ 0.7 | % | ISO 294 |
| Density | 1.20 | g/cm³ | ISO 1183 B |
| Melt Flow Rate | |||
| 300℃，1.20kg | 27 | g/10min | |
| Water absorption rate | |||
| 23℃，24hr，60% RH | 0.23 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 65 | MPa | ISO 527 |
| yield | 65 | MPa | ISO 527 |
| Nominal tensile fracture strain | 95 | % | ISO 527 |
| Tensile modulus | 2,000 | Mpa | ISO 527 |
| bending strength | 90 | MPa | ISO 178 |
| Bending modulus | 2,300 | MPa | ISO 178 |
| Rockwell hardness | 120/50 | R/M 级 | ISO 2039 |
| Taber abraser | 12 | mg (1000 rounds) | ASTM D1044 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| A50 | 145 | ℃ | ISO 306 |
| Hot deformation temperature | |||
| 1.8 MPa | 125 | ℃ | ISO 75 A |
| Linear coefficient of thermal expansion | 6,5 | x 10 -5 cm/cm/ºC | ASTM D 696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | 2.85 | 1 MHz | IEC 60250 |
| Dielectric constant | 2.91 | 100 Hz | IEC 60250 |
| Dielectric strength | |||
| 1.6 mm | 30E+5 | kV/mm | IEC 60243-1 |
| Dissipation factor | 0,0092 | 1 MHz | IEC 250 |
| Arc resistance | 110 | sec | ASTM D495 |
| Volume resistivity | 8×10^20 | ohms·cm | ASTM D257 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1,586 | ||
| Total luminous transmittance | 85~89 | % | ISO 13468 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-2 | 1.5mm | UL 94 |
| HB | > 2.40 mm | ||
| Extreme oxygen index | 28 | % | ISO 4589 |
| Hot wire ignition 1.46 mm | 3 | UL 94 | |
| Hot filament ignition test 1.60 mm | 875 | ℃ | IEC 695-2-13 |
| Hot filament ignition test 2.00 mm | 875 | ℃ | IEC 695-2-13 |
| Hot filament ignition test 3.00 mm | 875 | ℃ | IEC 695-2-13 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 40 | kJ/m² | ISO 179 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Melt Temperature | 270 ~ 310 | °C | |
| Mold temperature | 60 ~ 90 | °C | |
| Pre drying | 4 hours/120°C | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |