| About |
|---|
| UV, Steam and Long-term heat resistance, High strength&& |
| Product Description | |
|---|---|
| Supplier | Idemitsu |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Resistance to the steam,V-2 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 12.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| TD：1.00 mm | 0.50 to 0.70 | % | Internal Method |
| MD：1.0 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.23 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 80 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 125 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | |||
| MD | 6.5E-5 | 1/℃ | ISO 11359-2 |
| Relative temperature index | |||
| Electrical performance, 0.36 mm | 130 | ℃ | UL 746 |
| Impact mechanical performance, 0.36 mm | 125 | ℃ | UL 746 |
| 0.36 mm | 130 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | PLC 2 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.40 mm | V-2 | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.585 | ASTM D542 | |
| Transmittance | 90.0 | % | ISO 13468-1 |
| Haze | |||
| 3000 µm | 0.90 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | >PC< |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | ||
| M-level | 50 | ISO 2039-2 | |
| R-level | 120 | ISO 2039-2 | |
| tensile strength | |||
| yield | 65.0 | MPa | ISO 527-2 |
| Nominal tensile fracture strain | 95 | % | ISO 527-2 |
| Bending modulus | 2300 | MPa | ISO 178 |
| bending strength | 90.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 5.0 to 8.0 | hr | |
| Barrel rear temperature | 260 to 280 | °C | |
| Barrel middle temperature | 260 to 280 | °C | |
| Barrel front temperature | 260 to 280 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 24h |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |