| About |
|---|
| Flame-retardant V-0, UL746C: f1&& |
| Product Description | |
|---|---|
| Supplier | Idemitsu |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | V-1,HB,Flame Characteristics,5VB,V-0,Copolymer |
| Availabilitys | Africa & Middle East ,North America,Europe,Latin America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 11.0 | cm³/10min | ISO 1133 |
| Spiral flow length | 25.0 | cm | Internal Method |
| Shrinkage rate | Internal Method | ||
| TD：2.0 mm | 0.60 to 0.80 | % | Internal Method |
| MD：2.0 mm | 0.60 to 0.80 | % | Internal Method |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | ISO 62 |
| Outdoor applicability | |||
| Black | f1 | UL 746C | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 60.0 | MPa | ISO 527-2 |
| Nominal tensile fracture strain | 100 | % | ISO 527-2 |
| Bending modulus | 2100 | MPa | ISO 178 |
| bending strength | 90.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 45 | kJ/m² | ISO 179 |
| 23℃ | 75 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 600 | J/m | ASTM D256 |
| 0℃ | 700 | J/m | ASTM D256 |
| 23℃ | 750 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 123 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 138 | ℃ | ISO 75-2/B |
| Linear coefficient of thermal expansion | |||
| MD | 8.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | PLC 3 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm, except for black | HB | UL 94 | |
| 0.80 mm, black | V-1 | UL 94 | |
| 1.50 mm, all colors | V-0 | UL 94 | |
| 2.00 mm, all colors | 5VB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | >PC< |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 5.0 to 8.0 | hr | |
| Barrel rear temperature | 270 to 310 | °C | |
| Barrel middle temperature | 270 to 310 | °C | |
| Barrel front temperature | 270 to 310 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Mold Temperature: 176°F, Melt Temperature: 572°F, Injection Pressure: 1.45E+4 psi |
| 3. Thickness: 2mm / Width: 10mm |
| 4. 24h |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |