| About |
|---|
| It is 20% carbon fibre reinforced polyamide 6 compound, heat stabilised, good conductive and electrostatic properties&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Conductive,Antistatic property,Heat Stabilized,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 275℃，5 kg | 40.0 | cm³/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.5 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 52 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | 8.5 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 200 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 215 | ℃ | ISO 306/B |
| Melting temperature | 221 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+6 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+6 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 | |
| Burning rate | + | FMVSS 302 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Type | PA6, MHRZ, 14-140, CF20 | ISO 1874 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 210 | MPa | ISO 2039-1 |
| Tensile modulus | 14200 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 175 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 4.0 | % | ISO 527-2/5 |
| Bending modulus | 11500 | MPa | ISO 178 |
| bending strength | 240 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | < 80 | °C | |
| Recommended maximum moisture content | < 0.10 | % | |
| Proposed maximum recycled material ratio | 10 | % | |
| Processing (melt) temperature | 240 to 260 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Injection pressure | 80.0 to 110 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |