| It is 30% glass fibre reinforced polyamide 6 compound, heat stabilised.&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.35 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.003 | % | ISO 294-4 |
| TD | 0.013 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 1.5 | % | ISO 62 |
| Melt Flow Rate | |||
| 275℃，5.0kg | 50 | g/10min | ISO 1133 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 210 | ℃ | ISO 75-2/A |
| Melting temperature | 221 | ℃ | ISO 11357-3 |
| Vicat Softening Temp | |||
| B50, dry | 215 | ℃ | ISO 306 |
| Glowing wire flammability index | 550 | ℃ | PN-EN-60695-2-12 |
| Linear coefficient of thermal expansion |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+11 | Ω.cm | IEC 60093 |
| Surface resistance | 1.0E+16 | Ω.cm | IEC 60093 |
| Insulation strength | |||
| 28 | KV/mm | IEC 60243-1 | |
| Dissipation factor | |||
| Compared to the leakage tracing index | 500 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.80mm | HB | UL-94 | |
| 1.00mm | HB | UL-94 | |
| 1.60mm | HB | UL-94 | |
| 2.00mm | HB | UL-94 | |
| 3.20mm | HB | UL-94 | |
| 6.00mm | HB | UL-94 | |
| Igniting temperature of the hot wire | |||
| 1 mm | 725 | ℃ | IEC 60695-2-12 |
| 2 mm | 725 | ℃ | IEC 60695-2-12 |
| 6 mm | 725 | ℃ | IEC 60695-2-12 |
| Relative temperature of heating wire | |||
| 1.00mm | 700 | ℃ | IEC 60695-2-13 |
| 2.00mm | 700 | ℃ | IEC 60695-2-13 |
| 6.00mm | 700 | ℃ | IEC 60695-2-13 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 80 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 13 | kJ/m² | ISO 179/1eA |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| 205 | MPa | ISO 2039-1 | |
| tensile strength | |||
| 23℃ | 175 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 4 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 9000 | MPa | ISO 527-2 |
| bending strength | |||
| 3.50% strain, 23 ℃ | <=260 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 8500 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 75 -100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |