| About |
|---|
| PC/ABS alloy 20% glass fibres reinforced, high stiffness and thermal resistance.&& |
| Product Description | |
|---|---|
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High Heat Resistance,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 to 1.26 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 10 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.20 to 0.40 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| 23℃，24hr | 0.10 | % | ISO 62 |
| Saturation, 23 ℃ | 0.25 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 6000 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 75.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 2.0 | % | ISO 527-2/50 |
| Bending modulus | 5200 | MPa | ISO 178 |
| bending strength | 110 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 30 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃ | 100 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 118 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 134 | ℃ | ISO 306 |
| Ball pressure test | |||
| 125℃ | 通过 | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD：-30~30℃ | 4.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 2 mm | 24 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | |||
| Solution A | 200 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 | |
| Glowing wire flammability index | |||
| 2.0 mm | 650 | ℃ | IEC 60695-2-12 |
| Extreme oxygen index | 24 | % | ASTM D2863 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Ash Content | |||
| 750℃ | 20 | % | ISO 3451 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 1.0 | hr | |
| Processing (melt) temperature | 240 to 270 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |