| About |
|---|
| TAROLOX 10 Z2 is a Polybutylene Terephthalate (PBT) product. It can be processed by injection molding and is available in Europe. Characteristics include: Flame Rated Impact Modified Impact Resistant Medium Viscosity&& |
| Product Description | |
|---|---|
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | High impact resistance,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.26 to 1.28 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 250℃，1.20kg | 12 | g/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| TD | 1.6 to 1.8 | % | Internal Method |
| MD | 1.6 to 1.8 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| 23℃，24hr | 0.080 | % | ISO 62 |
| Saturation, 23 ℃ | 0.50 | % | ISO 62 |
| Granule Humidity | < 0.050 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2200 | MPa | ISO 527-1-2 |
| tensile strength | ISO 527-2/50 | ||
| yield | 55.0 | MPa | ISO 527-2/50 |
| fracture | 45.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | > 100 | % | ISO 527-2/50 |
| Bending modulus | 2100 | MPa | ISO 178 |
| bending strength | 70.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 10 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 45 | J/m | ASTM D256 |
| 23℃ | 85 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 55.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| A50 | 185 | ℃ | ISO 306/A50 |
| B50 | 165 | ℃ | ISO 306 |
| Ball pressure test | |||
| 165℃ | 通过 | IEC 60695-10-2 | |
| Melting temperature | 218 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD：-30~30℃ | 1.0E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 2 mm | 18 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | |||
| Solution A | > 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.00 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 | |
| Glowing wire flammability index | |||
| 2.0 mm | 650 | ℃ | IEC 60695-2-12 |
| Extreme oxygen index | 22 | % | ASTM D2863 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| — | 100 | °C | |
| Pre-drying equipment | 100 to 110 | °C | |
| Drying time | |||
| — | 1.0 to 2.0 | hr | |
| Pre-drying equipment | 3.0 | hr | |
| Processing (melt) temperature | 230 to 250 | °C | |
| Mold temperature | 50 to 70 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. TARO 002 |
| 3. 0.039 in/min |
| 4. 120°C/hr |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |