| PET medium viscosity 30% glass fibres reinforced, very good chemical resistance, good mechanical, thermal and electrical properties, low moisture absorption, good dimensional stability. Available: all colors, heat stabilized (H), release agent (W).&& |
| Product Description | |
|---|---|
| Generic | PET |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Good Electrical Properties,Good stripping performance,High Heat Resistance,Solvent resistance,Low moisture absorption,Heat Stabilized,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.55 to 1.57 | g/cm³ | ISO 1183 |
| Shrinkage rate | Internal Method | ||
| TD | 0.50 to 0.70 | % | Internal Method |
| MD | 0.20 to 0.30 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 0.050 | % | ISO 62 |
| Granule Humidity | < 0.030 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 10000 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 135 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 2.5 | % | ISO 527-2/50 |
| Bending modulus | 9000 | MPa | ISO 178 |
| bending strength | 220 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 46 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -20℃ | 70 | J/m | ASTM D256 |
| 23℃ | 85 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 246 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 225 | ℃ | ISO 75-2/A |
| Continuous use temperature | IEC 60216 | ||
| — | 140 | ℃ | IEC 60216 |
| — | 140 | ℃ | IEC 60216 |
| Vicat Softening Temp | |||
| B50 | 240 | ℃ | ISO 306 |
| Ball pressure test | |||
| 245℃ | 通过 | IEC 60695-10-2 | |
| Melting temperature | 256 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD：-30~30℃ | 3.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1 mm | 34 | kV/mm | ASTM D149 |
| Dielectric constant | 3.60 | IEC 60250 | |
| Compared to the leakage tracing index | |||
| Solution A | 250 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.00 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 | |
| Igniting temperature of the hot wire | |||
| 2 mm | 750 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 24 | % | ASTM D2863 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 130 | °C | |
| Processing (melt) temperature | 270 to 300 | °C | |
| Mold temperature | 90 to 130 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |