| About |
|---|
| Polyamide 66 medium viscosity 45% glass fibres reinforced, flame retardant UL94 V0, heat stabilized, very good flame proofing also at low thickness. Very high mechanical and thermal properties, very low shrinkage and high dimensional stability, high tracking resistance.&& |
| Product Description | |
|---|---|
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Low contractility,Flame Characteristics,Heat Stabilized,Electric mark,V-0 |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.61 to 1.63 | g/cm³ | ISO 1183 |
| Shrinkage rate | Internal Method | ||
| TD | 0.25 to 0.50 | % | Internal Method |
| MD | 0.15 to 0.30 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| 23℃，24hr | 0.40 | % | ISO 62 |
| Saturation, 23 ℃ | 3.0 | % | ISO 62 |
| Granule Humidity | < 0.15 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 12000 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 170 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 1.5 | % | ISO 527-2/50 |
| Bending modulus | 11000 | MPa | ISO 178 |
| bending strength | 230 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 8.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 40 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃ | 85 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 244 | ℃ | ISO 75-2/A |
| Continuous use temperature | 180 | ℃ | IEC 60216 |
| Vicat Softening Temp | |||
| B50 | 246 | ℃ | ISO 306 |
| Ball pressure test | |||
| 230℃ | 通过 | IEC 60695-10-2 | |
| Melting temperature | 250 to 256 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 2 mm | 28 | kV/mm | IEC 60243-1 |
| Dielectric constant | 3.70 | IEC 60250 | |
| Compared to the leakage tracing index | |||
| Solution A | > 400 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | V-0 | UL 94 | |
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 1.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 1 mm | 875 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 36 | % | ASTM D2863 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Ash Content | |||
| 850℃ | 45 | % | ISO 3451 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 1.0 | hr | |
| Processing (melt) temperature | 270 to 300 | °C | |
| Mold temperature | 90 to 110 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. TARO 002 |
| 3. 0.039 in/min |
| 4. 120°C/hr |
| 5. Short term |
| 6. 1 hr |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |