| About |
|---|
| PA6 mineral filled 30%, good dimensional stability, uniform shrinkage in all directions, good surface finish and good mechanical and thermal properties. Available: all colors, UV-stabilized (L), heat-stabilized (H), release agent (W).&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good surface appearance,Good Dimensional Stability,Good stripping performance,Heat Stabilized,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 to 1.38 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 250℃，2.16kg | 8.0 | g/10min | ASTM D1238，ISO 1133 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.40 to 0.60 | % | ASTM D955 |
| TD | 0.40 to 0.60 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.90 to 1.0 | % | ASTM D570，ISO 62 |
| saturated | 6.5 | % | ASTM D570 |
| Saturation, 23 ℃ | 6.5 | % | ISO 62 |
| Granule Humidity | < 0.10 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 4.5 | kJ/m² | ASTM D256，ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 42 | J/m | ASTM D256，ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 185 | ℃ | ASTM D648，ISO 75-2/A |
| Continuous use temperature | IEC 60216 | ||
| — | 70.0 | ℃ | IEC 60216 |
| — | 100 | ℃ | IEC 60216 |
| — | 110 | ℃ | IEC 60216 |
| — | 150 | ℃ | IEC 60216 |
| Vicat Softening Temp | |||
| B50 | 210 | ℃ | ISO 306/B50 , ASTM D1525 7 |
| Ball pressure test | |||
| 165℃ | 通过 | VDE 0470 | |
| Melting temperature | 222 | ℃ | ASTM D211，ISO 121 |
| Linear coefficient of thermal expansion | |||
| MD：-30~30℃ | 4.5E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 | |
| Igniting temperature of the hot wire | |||
| 2 mm | 750 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 24 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 115 | ASTM D785 | |
| Tensile modulus | 6800 | MPa | ASTM D638 , ISO 527-2 |
| tensile strength | |||
| fracture | 80.0 | MPa | ASTM D638 , ISO 527-2 |
| Tensile strain | |||
| fracture | 2.6 | % | ASTM D638 , ISO 527-2 |
| Bending modulus | 6500 | MPa | ASTM D790 , ISO 178 |
| bending strength | |||
| — | 126 | MPa | ISO 178 |
| fracture | 126 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| — | 80 to 90 | °C | |
| Pre-drying equipment | 80 to 100 | °C | |
| Drying time | |||
| — | 2.0 | hr | |
| Pre-drying equipment | 3.0 | hr | |
| Processing (melt) temperature | 230 to 270 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 6x4x50 mm |
| 3. 20000 hrs |
| 4. Short Term |
| 5. Heat Stabilized, 20000 hrs |
| 6. Heat Stabilized, Short Term |
| 7. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |