| About |
|---|
| TASNEE 100橙色是高密度聚乙烯橙色树脂。 该产品被归类为PE 100，具有卓越的抗环境应力开裂性能（ESCR）和非常好的长期静液压强度。 它具有非常高的抗冲击强度和优异的可加工性。用于气体分配管道 |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good flexibility,High ESCR |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.951 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，5.0kg | 0.23 | g/10min | ISO 1133 |
| 190℃，21.6kg | 6.4 | g/10min | ISO 1133 |
| Staudinger index Jg | 380 | Ml/g | ISO 1628 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 3 seconds | 62 | ISO 868 | |
| Tensile modulus | |||
| 23℃，1 mm/min | 850 | MPa | ISO 527-1 |
| tensile strength | |||
| Yield, 23 ℃, 50 mm/min | 23 | MPa | ISO 527-1-2 |
| Tensile strain | |||
| Yield, 23 ℃, 50 mm/min | 9 | % | ISO 527-1 |
| Tensile creep modulus, 1h [test pressure, MPa] | 850 [2.0] | MPa | ISO 899-1 |
| Tensile creep modulus, 1000h [test pressure, MPa] | 350 [2.0] | MPa | ISO 899-1 |
| Maximum elongation | |||
| transverse | >350 | % | EN 638 |
| MRS classification | 10 | MPa | ISO/TR 9080 |
| bending strength | |||
| 3.50% strain | 20 | MPa | ISO 178 |
| Full notch creep test | |||
| 4.0 MPa，2% Arkopal N 100，80℃ | >1000 | h | ISO 16770 |
| Bending creep modulus | |||
| 4-point loading method, 1 minute | 1100 | MPa | DIN 19537-2 |
| 4-point loading method, 24 hours | 560 | MPa | DIN 19537-2 |
| 4-point loading method, 2000 hours | 330 | MPa | DIN 19537-2 |
| Oxidation induction time | |||
| OIT，210℃ | ≥ 30 | min | EN 728 |
| Odor threshold | <2 | EN1622/EN1240 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 29 | kJ/m² | ISO 179 |
| -30℃ | 15 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| B50 | 74 | ℃ | ISO 306 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |