| TASNEE LD 0725N是一种熔体流动速率为0.75 g / 10min（190°C / 2.16kg）的低密度聚乙烯。无添加剂，具有合适的分子结构，可以制成具有优异机械性能的薄膜。可以在为聚乙烯设计的所有类型的挤出机上轻松加工。 建议熔体温度在170-220℃的范围内。 该膜的优异性能是以2：1的吹胀比和推荐的膜厚范围从25至100μm实现的。 典型应用： 中型收缩包装，中型袋和袋，食品包装薄膜。 产品特性： 良好的薄膜强度，良好的光学性能，良好的加工性。 |
| Product Description | |
|---|---|
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Alkali resistant,High impact resistance,Food contact compliance,Acidproof,Good tear strength,Puncture Resistant,High shrinkage |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.75 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 260 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Flow/TD | 26 / 24 | MPa | ISO 527-1,-3 |
| yield | 11 | MPa | ISO 527-1-2 |
| Tensile strain | |||
| 断裂，流动 / 横向 | 300 / 600 | % | ISO 527-1,-3 |
| Drop hammer impact | |||
| 50 µm | 150 | g | ASTM D1709 |
| friction coefficient | > 80 | % | ISO 8295 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | < 8 | % | ASTM D1003 |
| gloss | |||
| 20 ° | > 40 | GU | ASTM D 2457 |
| 60° | > 90 | GU | ASTM D 2457 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 111 | ℃ | ISO 3146 |
| Vicat Softening Temp | |||
| A50 | 96 | ℃ | ISO 306 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |