| TASNEE LD 1925AS是一种熔体流动速率为1.9 g / 10min（190°C / 2.16kg）的低密度聚乙烯。主要用于收缩膜应用。 它含有滑爽剂和防粘连添加剂，具有合适的分子结构，可以生产出具有优异机械性能的薄膜.TASNEE LD 1925AS可以很容易地在所有类型的聚乙烯挤出机上加工。 建议熔体温度在160-190℃的范围内。 吹膜比为2：1，推荐膜厚范围为25至60μm。 典型应用： 包装袋，收缩膜，食品包装，表面保护。 产品特性 特点：防粘连滑爽添加剂，良好的光学性能，良好的加工性，低摩擦。 |
| Product Description | |
|---|---|
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Alkali resistant,Food contact compliance,Acidproof,Good tear strength,Puncture Resistant,High shrinkage |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.925 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.90 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 260 | MPa | ISO 527-1 |
| tensile strength | |||
| Flow/TD | 26 / 18 | MPa | ISO 527-1-2 |
| yield | 11 | MPa | ISO 527-1-2 |
| Tensile strain | |||
| 断裂，流动 / 横向 | 250 / 600 | % | ISO 527-1 |
| Drop hammer impact | |||
| 50 µm | 110 | g | ASTM D1709 |
| friction coefficient | 20 | % | ISO 8295 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | < 7 | % | ASTM D1003 |
| gloss | |||
| 20 ° | > 50 | GU | ASTM D 2457 |
| 60° | > 100 | GU | ASTM D 2457 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 111 | ℃ | ISO 3146 |
| Vicat Softening Temp | |||
| A50 | 94 | ℃ | ISO 306 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |