TASNEE LD 4025AS

About
TASNEE LD 4025AS是一种低密度聚乙烯，熔体流动速率为4.0 g / 10min（190°C / 2.16kg）。主要推荐用于具有高透明度薄膜应用的薄规格。它含有滑爽剂和防粘连添加剂，并具有合适的分子结构，可以生产具有优异机械性能的薄膜。TASNEE LD 4025AS可以很容易地在所有类型的聚乙烯挤出机上加工。建议熔体温度在150-190℃的范围内。吹胀比达到2.5：1，推荐膜厚范围从15到40μm。典型应用：收缩膜，食品包装膜，吹塑膜和流延膜。产品特性特性：防粘和滑爽添加剂，良好的光学性能，良好的加工性，低摩擦力和耐磨性良好的刚度。

About

TASNEE LD 4025AS是一种低密度聚乙烯，熔体流动速率为4.0 g / 10min（190°C / 2.16kg）。主要推荐用于具有高透明度薄膜应用的薄规格。它含有滑爽剂和防粘连添加剂，并具有合适的分子结构，可以生产具有优异机械性能的薄膜。TASNEE LD 4025AS可以很容易地在所有类型的聚乙烯挤出机上加工。建议熔体温度在150-190℃的范围内。吹胀比达到2.5：1，推荐膜厚范围从15到40μm。
典型应用：
收缩膜，食品包装膜，吹塑膜和流延膜。
产品特性
特性：防粘和滑爽添加剂，良好的光学性能，良好的加工性，低摩擦力和耐磨性
良好的刚度。

Product Description
Generic	LDPE
Material Status	Commercial: Active
Features	Alkali resistant,Food contact compliance,Acidproof,Good tear strength,Puncture Resistant,High shrinkage
Availabilitys	Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.925	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	4.0	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	260	MPa	ISO 527-1
tensile strength
Flow/TD	22 / 15	MPa	ISO 527-1-2
yield	11	MPa	ISO 527-1-2
Tensile strain
断裂，流动 / 横向	300 / 600	%	ISO 527-1
Drop hammer impact
50 µm	100	g	ASTM D1709
friction coefficient	< 20	%	ISO 8295

optical performance	Nominal value	Unit	Test method
Haze	< 9	%	ASTM D1003
gloss
20 °	> 60	GU	ASTM D 2457
60°	> 105	GU	ASTM D 2457

THERMAL	Nominal value	Unit	Test method
Melting temperature	111	℃	ISO 3146
Vicat Softening Temp
A50	92	℃	ISO 306

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.