| Main features excellent tensile strength heat stabilized Target Industries automotive industry business machines mechanical engineering precision engineering&& |
| Product Description | |
|---|---|
| Supplier | Ensinger |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Tensile Strength,Heat Stabilized |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.48 | g/cm³ | |
| Apparent density | 0.69 | g/cm³ | ISO 60 |
| Melt Flow Rate | |||
| 280℃，5.0kg | 50 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 280℃，5 kg | 38.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 0.98 | % | |
| MD | 0.31 | % | |
| Viscosity (H2SO4 (sulfuric acid)) | 143 | cm³/g | ISO 307 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 10000 | MPa | ISO 527-2/50 |
| tensile strength | 160 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 2.5 | % | ISO 527-2/50 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | 50 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 255 | ℃ | ISO 75-2/A |
| Glass transition temperature | |||
| — | 5.00 | ℃ | |
| — | 72.0 | ℃ | |
| Melting temperature | 260 | ℃ | DIN 53765 |
| Operating temperature | |||
| long-term | 110 | ℃ | |
| short-term | 170 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 to 8.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Processing (melt) temperature | 260 to 310 | °C | |
| Mold temperature | 90 to 150 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Moist |
| 3. Dry |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |