| Main features detectable via metal detector x-ray detectable |
| Product Description | |
|---|---|
| Supplier | Ensinger |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Metal Detectable |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.28 | g/cm³ | |
| Apparent density | 0.68 | g/cm³ | ISO 60 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 39 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 37.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 1.5 | % | |
| MD | 1.4 | % | |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | < 0.10 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2200 | MPa | ISO 527-2/50 |
| tensile strength | 25.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 30 | % | ISO 527-2/50 |
| Bending modulus | 1800 | MPa | ISO 178 |
| bending strength | 43.0 | MPa | ISO 178 |
| Bending strain | 5.0 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | 20 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -18.0 | ℃ | DIN 53765 |
| Melting temperature | 165 | ℃ | DIN 53765 |
| Operating temperature | |||
| long-term | 100 | ℃ | |
| short-term | 130 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | HB | IEC 60695-11-10, -20 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 70 to 100 | °C | |
| Drying time | 2.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Processing (melt) temperature | 200 to 260 | °C | |
| Mold temperature | 40 to 100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |