| About |
|---|
| Main features developed for the LPKF-LDS® process high thermal conductivity Target Industries automotive industry electrical engineering LED lighting technology mechanical engineering&& |
| Product Description | |
|---|---|
| Supplier | Ensinger |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Thermal conductivity |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.54 | g/cm³ | |
| Melt Flow Rate | |||
| 300℃，5.0kg | 32 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 300℃，5 kg | 20.6 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 0.60 | % | |
| MD | 0.60 | % | |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | < 0.10 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 9000 | MPa | ISO 527-2/50 |
| tensile strength | 43.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 0.50 | % | ISO 527-2/50 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | 5.0 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 222 | ℃ | ISO 75-2/A |
| Glass transition temperature | 100 to 140 | ℃ | DIN 53765 |
| Melting temperature | 285 to 315 | ℃ | DIN 53765 |
| Linear coefficient of thermal expansion | |||
| MD：50~100℃ | 3.3E-5 | 1/℃ | |
| MD：100~150℃ | 5.3E-5 | 1/℃ | |
| MD：150~200℃ | 7.7E-5 | 1/℃ | |
| TD：50~100℃ | 3.4E-5 | 1/℃ | |
| TD：100~150℃ | 5.9E-5 | 1/℃ | |
| TD：150~200℃ | 9.4E-5 | 1/℃ | |
| specific heat | 1090 | J/kg/℃ | DIN EN 821 |
| Thermal conductivity coefficient | |||
| — | 1.3 | W/m/K | |
| — | 4.3 | W/m/K | |
| Operating temperature | |||
| long-term | 150 | ℃ | |
| short-term | 250 | ℃ | |
| Thermal diffusion coefficient | |||
| In-plane | 2.53 | cSt | |
| Through-plane | 0.770 | cSt |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 4.7E+12 | ohms | DIN EN 61340 |
| Volume resistivity | 5.2E+13 | ohms·cm | DIN EN 61340 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | HB | IEC 60695-11-10, -20 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Adhesive strength | |||
| metal path | 20.2 | MPa | |
| Lazer Marking | |||
| Forward moving | 2.0 to 3.0 | m/sec | |
| Frequency | 100 to 200 | kHz | |
| Power | 2.00 to 6.00 | Watts |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Processing (melt) temperature | 320 to 340 | °C | |
| Mold temperature | 150 to 170 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Through-plane |
| 3. In-plane |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |