TECAPEEK® TECAPEEK®

About
TECAPEEK® stock shapes are made exclusively with Victrex PEEK polymer. TECAPEEK is a unique, semi-crystalline, high temperature engineering thermoplastic. It is an excellent material for a wide spectrum of applications where thermal, chemical, and combustion properties are critical to performance. Especially significant in this regard is TECAPEEK’s ability to retain its flexural and tensile properties at very high temperatures in excess of 250°C (482°F). The addition of glass fiber or carbon fiber reinforcements enhances the mechanical and thermal properties of the basic TECAPEEK® material. TECAPEEK™s exceptional property profile enables it to be utilized in many of the most critical areas in general industry, as well as in the automotive, marine, nuclear, oil well, electronics, medical and aerospace fields.&&

About

TECAPEEK® stock shapes are made exclusively with Victrex PEEK polymer. TECAPEEK is a unique, semi-crystalline, high temperature engineering thermoplastic. It is an excellent material for a wide spectrum of applications where thermal, chemical, and combustion properties are critical to performance. Especially significant in this regard is TECAPEEK’s ability to retain its flexural and tensile properties at very high temperatures in excess of 250°C (482°F). The addition of glass fiber or carbon fiber reinforcements enhances the mechanical and thermal properties of the basic TECAPEEK® material. TECAPEEK™s exceptional property profile enables it to be utilized in many of the most critical areas in general industry, as well as in the automotive, marine, nuclear, oil well, electronics, medical and aerospace fields.&&

Product Description
Supplier	Ensinger
Generic	PEEK
Material Status	Commercial: Active
Features	High impact resistance,Low smoke,Hydrolysis stability,Gamma radiation,High Heat Resistance,Hypocrystalline,Good wear resistance,Solvent resistance,V-0
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.30	g/cm³	ASTM D792
Water absorption rate			ASTM D570
23℃，24hr	0.50	%
Saturation, 23 ℃	0.50	%

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	51	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed, 6.35 mm	160	℃	ASTM D648
Continuous use temperature	260	℃
Melting temperature	334	℃
Linear coefficient of thermal expansion
MD	4.7E-5	1/℃	ASTM D696
Thermal conductivity coefficient	0.25	W/m/K	ASTM C177

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	1.0E+16	ohms	ASTM D257
Volume resistivity
23℃	4.9E+16	ohms·cm	ASTM D257
Dielectric strength	7.5	kV/mm	ASTM D149

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	V-0		UL 94

Supplementary information	Nominal value	Unit
Pressure limiting speed
1200 in/min，20℃	170000	psi·fpm
memo_intro

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
M-level	99		ASTM D785
Tensile modulus
1% secant, 23 ℃	4480	MPa	ASTM D638
tensile strength
Yield, 23 ℃	110	MPa	ASTM D638
Tensile strain			ASTM D638
Yield, 23 ℃	4.9	%
Fracture, 23 ℃	40	%
Bending modulus
23℃	4140	MPa	ASTM D790
bending strength
23℃	179	MPa	ASTM D790
compressive strength
23℃	118	MPa	ASTM D695
shear strength
23℃	52.4	MPa	ASTM D3846
friction coefficient	0.18

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.