| High mechanical strength and stiffness High thermal stability High toughness at low temperatures Excellent sliding friction behavior Optimal flow characteristics for challenging applications Suitable for low-warpage injection molding parts Also “cross-linkable” available Typical Applications Automotive: Radiator grills, exterior door handles, door sills, door-mirror housings, wheel covers, steering wheels, fastening clips, gearshift-lever housings, shift links, headlamp housings, power and fuse boxes, front-End-Modules, bumper stiffener, air intake modules, engine covers “Beauty-Cover”, valve bonnet and cylinder head covers, chain guides, toothed belt covers, ventilation and cooling systems… Household: Chair frames, furniture casters, craft toll shafts… Sanitation: Handles, fittings, fixtures and fans Plumbing: Wall dowels , fasteners, clamps for cables and pipes&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low warping,Good liquidity,Low temperature toughness,Heat Stabilized,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.70 | % | ISO 294-4 |
| MD | 0.20 | % | ISO 294-4 |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 7.5 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 2.4 | % | ISO 62 |
| Viscosity number | 150 | cm³/g | ISO 307 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 6.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 60 | kJ/m² | ISO 179/1eU |
| 23℃ | 65 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 210 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 200 | ℃ | ISO 75-2/A |
| 8.0 MPa, unannealed | 60.0 | ℃ | ISO 75-2/C |
| Vicat Softening Temp | |||
| B120 | 200 | ℃ | ISO 306/B120 |
| Melting temperature | 220 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：23~80℃ | 3.0E-5 to 5.0E-5 | 1/℃ | ISO 11359-2 |
| TD：23~80℃ | 9.0E-5 to 1.1E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1 mm | 35 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 1 MHz | 3.70 | IEC 60250 | |
| Compared to the leakage tracing index | |||
| Solution A | 550 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | 145 | MPa | ISO 2039-1 |
| Tensile modulus | 5500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 110 | MPa | ISO 527-2/50 |
| fracture | 110 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| yield | 4.0 | % | ISO 527-2/50 |
| fracture | 4.0 | % | ISO 527-2/5 |
| Bending modulus | 4500 | MPa | ISO 178 |
| bending strength | 150 | MPa | ISO 178 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |