| About |
|---|
| Product Description | |
|---|---|
| Supplier | DOMO |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Laser engraving |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.32 | g/cm³ | |
| Water absorption rate | |||
| 23℃，24hr | 0.90 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 8400 | MPa | |
| Tensile stress (fracture, 23 ° C) | 165 | MPa | |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | |
| Bending modulus | |||
| 23℃ | 7300 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 10 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 23℃ | 57 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 8.5 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 255 | ℃ | |
| Melting temperature | 263 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | |
| Solution B | 525 | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glowing wire flammability index | |||
| 1.6 mm | 650 | ℃ | |
| Extreme oxygen index | 23 | % |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 | °C | |
| Recommended maximum moisture content | 0.20 | % | |
| Temperature at the rear of the barrel | 270 to 280 | °C | |
| Temperature in the middle of the barrel | 275 to 285 | °C | |
| Front temperature of material barrel | 280 to 290 | °C | |
| Mold temperature | 70 to 100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |