| About |
|---|
| Product Description | |
|---|---|
| Supplier | DOMO |
| Generic | PA66 |
| Material Status | Commercial: Negative |
| Features | Halogen free,Heat Stabilized,Flame Characteristics |
| Availabilitys | North America,Africa & Middle East ,Europe,Asia Pacific,Latin America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 | g/cm³ | ISO 1183 |
| Forming shrinkage rate | |||
| MD | 0.3 – 0.5 | % | ISO 294-4, 2577 |
| TD | 0.6 – 0.8 | % | ISO 294-4, 2577 |
| viscosity | |||
| 96% H2SO4 | 145 | cm³/g | ISO 307 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 1 mm/min | 9500 | MPa | ISO 527-1/-2 |
| Tensile stress | |||
| 5 mm/min | 130 | MPa | ISO 527-1/-2 |
| Tensile strain | |||
| 5 mm/min | 3 | % | ISO 527-1/-2 |
| Bending modulus | |||
| 2 mm/min | 8500 | MPa | ISO 178 |
| bending strength | |||
| 2 mm/min | 190 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy impact strength | |||
| 23°C | 50 | KJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23°C | 8 | kJ/m² | ISO 179/1eA |
| Izod notched impact strength | |||
| 23°C | 45 | KJ/m² | ISO 180/1U |
| Impact strength of cantilever beam notch | |||
| 23°C | 7 | KJ/m² | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| 10°C/min | 262 | ℃ | ISO 11357-1 |
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 250 | ℃ | ISO 75 |
| 1.80 MPa, unannealed | 230 | ℃ | ISO 75 |
| Vicat Softening Temp | |||
| 50°C/h – 50N | 245 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1E+16 | ||
| Surface resistivity | 1E+14 | ||
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | IEC 60112 |
| PLC 0 | PLC | Solution A |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 1-3 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 1-3 mm | 750 | ℃ | IEC 60695-2-13 |
| Burning rate | |||
| 1 mm | ＜100 | mm/min | FMVSS 302 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 75 – 85 | °C | |
| Drying time | 2 – 4 | h | |
| Processing (melt) temperature | 270 – 290 | °C | |
| Mold temperature | 80 – 100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |