TECHNYL® A 60G1 V30 GREY R7035 LPU

About
TECHNYL® A 60G1 V30 Grey R7035 LPU is a polyamide 66 based on a non-halogenated flame retardant system, reinforced with 30% of glass fiber, heat stabilized, laser markable for injection moulding. This grade offers excellent flame retardancy properties (UL 94, 5VA, GWIT) combined with excellent processing, mechanical and electrical performance. It can withstand temperatures of 160°C for over 6000 hours and has a UL F1 rating for weatherability resistance&&

About

TECHNYL® A 60G1 V30 Grey R7035 LPU is a polyamide 66 based on a non-halogenated flame retardant system, reinforced with 30% of glass fiber, heat stabilized, laser markable for injection moulding. This grade offers excellent flame retardancy properties (UL 94, 5VA, GWIT) combined with excellent processing, mechanical and electrical performance. It can withstand temperatures of 160°C for over 6000 hours and has a UL F1 rating for weatherability resistance&&

Product Description
Supplier	DOMO
Generic	PA66
Material Status	Commercial: Active
Features	Halogen free,UV Laser Markable
Availabilitys	Africa & Middle East ,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.46	g/cm³
Melt Flow Rate
275℃，2.16kg	11	g/10min
Water absorption rate
23℃，24hr	0.63	%
Saturation, 23 ℃	4.0	%
Equilibrium, 23 ℃, 50% RH	1.7	%
Outdoor applicability
whole	f1

MECHANICAL	Nominal value	Unit
Tensile modulus
23℃	10900	MPa
tensile strength
Fracture, 23 ℃	115	MPa
Tensile strain
Fracture, 23 ℃	1.8	%
Bending modulus
23℃	10600	MPa
bending strength
23℃	170	MPa

IMPACT	Nominal value	Unit
Charpy Unnotch Impact strength
-30℃	30	kJ/m²
23℃	32	kJ/m²
Impact strength of cantilever beam notch
23℃	85	J/m

THERMAL	Nominal value	Unit	Test method
Melting temperature	262	℃

Electrical performance	Nominal value	Unit
Surface resistivity	2.0E+15	ohms
Volume resistivity	6.0E+14	ohms·cm
Dielectric strength
0.8 mm	38	kV/mm
Compared to the leakage tracing index
Solution A	600	V

FLAME CHARACTERISTICS	Nominal value	Unit
Flame retardant level
0.80 mm	V-0
1.60 mm
3.20 mm
Glowing wire flammability index
0.80 mm	960	℃
1.6 mm	960	℃
3.2 mm	960	℃
Igniting temperature of the hot wire
0.8 mm	775	℃
Extreme oxygen index	33	%
French Fire Index	F3
French Smoke Index	I3

Supplementary information	Nominal value	Unit	Test method
European Railway Certification
R22	HL3
R23	HL3

Process Conditions
Injection	Nominal value	Unit	Test method
Injection instructions	Nominal value	Unit	Test method
drying temperature	80	°C
Recommended maximum moisture content	0.20	%
Temperature at the rear of the barrel	265 to 275	°C
Temperature in the middle of the barrel	265 to 275	°C
Front temperature of material barrel	270 to 280	°C
Mold temperature	60 to 90	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.