| About |
|---|
| TECHNYL® C 206F Natural is an unreinforced polyamide PA6, standard for fast injection cycles, for injection moulding. This grade has high fluidity and a good mould release.&& |
| Product Description | |
|---|---|
| Supplier | DOMO |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good stripping performance,Quick molding cycle,Good liquidity |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | |
| Water absorption rate | |||
| 23℃，24hr | 1.6 | % | |
| Equilibrium, 23 ℃, 50% RH | 3.3 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 3000 | MPa | |
| tensile strength | |||
| Yield, 23 ℃ | 85.0 | MPa | |
| Fracture, 23 ℃ | 50.0 | MPa | |
| Tensile strain | |||
| Yield, 23 ℃ | 4.0 | % | |
| Fracture, 23 ℃ | 15 | % | |
| Bending modulus | |||
| 23℃ | 2800 | MPa | |
| bending strength | |||
| 23℃ | 100 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 4.0 | kJ/m² | |
| 23℃ | 5.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 | ||
| Impact strength of cantilever beam notch | |||
| 23℃ | 5.0 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 60.0 | ℃ | |
| Melting temperature | 222 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 | ohms | |
| Volume resistivity | 1.0E+15 | ohms·cm | |
| Dielectric strength | |||
| 2 mm | — | kV/mm | |
| Relative permittivity | 3.40 | ||
| Dissipation factor | 0.023 | ||
| Compared to the leakage tracing index | |||
| Solution A | 600 | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | V-2 | ||
| Igniting temperature of the hot wire | |||
| 0.8 mm | 675 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Injection instructions | Nominal value | Unit | Test method |
| drying temperature | 80 | °C | |
| Recommended maximum moisture content | 0.20 | % | |
| Temperature at the rear of the barrel | 230 to 235 | °C | |
| Temperature in the middle of the barrel | 235 to 240 | °C | |
| Front temperature of material barrel | 235 to 245 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |