TECHNYL® C 216 V35 NATURAL

About
TECHNYL® C 216 V35 Natural is a polyamide PA6, reinforced with 35 % of glass fibre, for injection moulding. This grade has good mechanical properties and offering an excellent combination between thermal and mechanical properties.&&

Product Description
Supplier	DOMO
Generic	PA6
Material Status	Commercial: Negative
Features	Good Dimensional Stability,Good stripping performance,Good liquidity
Availabilitys	Africa & Middle East ,Latin America,Europe,North America,Asia Pacific
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.38	g/cm³	ISO 1183
Forming shrinkage rate
parallel	0.2 – 0.4	%	ASTM D294-4
normal	0.8 – 1	%	ASTM D294-4

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
1 mm/min	10800	MPa	ISO 527-1/-2
Tensile stress
fracture	185	MPa	ISO 527-1/-2
Tensile strain
fracture	3	%	ISO 527-1/-2
Bending modulus
2 mm/min	10000	MPa	ISO 178
bending strength
2 mm/min	275	MPa	ISO 178
Rockwell hardness	122	R Scale	ISO 2039/2

IMPACT	Nominal value	Unit	Test method
Charpy impact strength
23°C	90	KJ/m²	ISO 179/1eU
-30°C	85	KJ/m²	ISO 179/1eU
Charpy Notched Impact Strength
23°C	14	kJ/m²	ISO 179/1eA
-30°C	12	kJ/m²	ISO 179/1eA
Izod notched impact strength
23°C	85	kJ/m²	ISO 180/1eU
Impact strength of cantilever beam notch
23°C	15	kJ/m²	ISO 180/1eA

THERMAL	Nominal value	Unit	Test method
Melting temperature
10°C/min	221	℃	ISO 11357-3
Hot deformation temperature
0.45 MPa, unannealed	220	℃	ISO 75
1.80 MPa, unannealed	210	℃	ISO 75
Vicat Softening Temp
50°C/h – 50N	215	℃	ISO 306

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	1E+13	ohm·cm	IEC 62631-3-1
Surface resistivity	1E+14	ohm	IEC 62631-3-1
Compared to the leakage tracing index
Solution A	400	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level
1.5 mm	HB		UL 94
Glowing wire flammability index
1.5 mm	650	℃	IEC 60695-2-12
Burning rate
FMVSS, 1 mm	＜100		FMVSS 302

Process Conditions
Injection	Nominal value	Unit	Test method
drying temperature	80	°C
Recommended maximum moisture content	0.20	%
Temperature at the rear of the barrel	230 – 235	°C
Temperature in the middle of the barrel	235 – 240	°C
Front temperature of material barrel	240 – 250	°C
Mold temperature	60 – 90	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.