TECHNYL® C 216 V40 BLACK Z

About
TECHNYL® C 216 V40 Black Z is a polyamide 6, reinforced with 40% of glass fibre, for injection moulding. This grade has good mechanical properties and offering an excellent combination between thermal and mechanical properties.&&

Product Description
Supplier	DOMO
Generic	PA6
Material Status	Commercial: Active
Features	HB
Availabilitys	North America,Europe,Africa & Middle East
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.45	g/cm³	ISO 1183/A
Water absorption rate
Saturation, 23 ℃	4.5	%	ISO 62
Equilibrium, 23 ℃, 50% RH	1.9	%	ISO 62
23℃，24hr	0.80	%	ISO 62

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
23℃	13000	MPa	ISO 527-2/1A
tensile strength
Fracture, 23 ℃	190	MPa	ISO 527-2/1A
Tensile strain
Fracture, 23 ℃	2.8	%	ISO 527-2
Bending modulus
23℃	11800	MPa	ISO 178
bending strength
23℃	300	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	15	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength
23℃	85	kJ/m²	ISO 179/1eU
23℃	60	kJ/m²	ISO 179/1fU
Impact strength of cantilever beam notch
23℃	14	kJ/m²	ISO 180
Notched impact strength of cantilever beam
23℃	75	kJ/m²	ISO 180/1U

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	214	℃	ISO 75-2/Af
Melting temperature	222	℃	ISO 11357-3

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	1.0E+14	ohms	IEC 60093
Volume resistivity	1.0E+15	ohms·cm	IEC 60093
Dielectric strength
2 mm	—	kV/mm	IEC 60243-1
Dissipation factor	0.020		IEC 60250
Compared to the leakage tracing index			IEC 60112
Solution A	600	V	IEC 60112
Solution B	475	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level			UL 94
0.40 mm	HB		UL 94
0.80 mm	HB		UL 94
1.60 mm	HB		UL 94
3.20 mm	HB		UL 94
Glowing wire flammability index			IEC 60695-2-12
1.6 mm	650	℃	IEC 60695-2-12
3.2 mm	650	℃	IEC 60695-2-12

Process Conditions
Injection	Nominal value	Unit	Test method
drying temperature	80	°C
Recommended maximum moisture content	0.20	%
Temperature at the rear of the barrel	235 to 240	°C
Temperature in the middle of the barrel	240 to 250	°C
Front temperature of material barrel	250 to 260	°C
Mold temperature	60 to 90	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.