TECHNYL® C 216 V50 NATURAL

About
TECHNYL® C 216 V50 Natural is a polyamide 6, reinforced with 50% of glass fibre, for injection moulding. This grade offers high mechanical strength, good surface aspect for injection moulding.&&

Product Description
Supplier	DOMO
Generic	PA6
Material Status	Commercial: Negative
Features	Good Dimensional Stability,Good Rigidity,Good stripping performance
Availabilitys	Africa & Middle East ,Europe,Latin America,Asia Pacific,North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.56	g/cm³	ISO 1183
Water absorption rate
23°C，50% RH	2.2 – 2.4	%	ISO 62
23°C，24 hr	1.4 – 1.5	%	ISO 62
saturated	6.2	%	ISO 62
Shrinkage rate
MD	0.2 – 0.4	%	ISO 294-4, 2577
TD	0.7 – 0.9	%	ISO 294-4, 2577
Melt Volume Rate
275°C，5kg	30	cm³/10min	ISO 1133
Viscosity value
96% H2SO4	125	cm³/g	ISO 307

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
1 mm/min	16500	MPa	ISO 527-1/-2
Tensile stress
5 mm/min	230	MPa	ISO 527-1/-2
Tensile strain
5 mm/min	3	%	ISO 527-1/-2
Bending modulus
2 mm/min	15000	MPa	ISO 178
bending strength
2 mm/min	350	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy impact strength
23°C	100	KJ/m²	ISO 179/1eU
-30°C	90	KJ/m²	ISO 179/1eU
Charpy Notched Impact Strength
23°C	20	kJ/m²	ISO 179/1eA
-30°C	15	kJ/m²	ISO 179/1eA
Izod notched impact strength	95	KJ/m²	ISO 180/1U
Impact strength of cantilever beam notch
23°C	19	KJ/m²	ISO 180/1A

THERMAL	Nominal value	Unit	Test method
Melting temperature	221	℃	ISO 11357-1
Hot deformation temperature
0.45 MPa	220	℃	ISO 75
1.80 MPa	210	℃	ISO 75
Vicat Softening Temp
50°C/h – 50N	215	℃	ISO 306

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	1E+13	ohm·cm	IEC 62631-3-1
Surface resistivity	1E+14	ohm	IEC 62631-3-1

FLAME CHARACTERISTICS	Nominal value	Test method
Flame retardant level
0.75mm	HB	UL 94
Burning rate
FMVSS，1mm	＜100mm/min	FMVSS 302

Process Conditions
Injection	Nominal value	Unit	Test method
drying temperature	75 – 85	°C
Recommended maximum moisture content	0.20	%
Temperature at the rear of the barrel	235 – 240	°C
Temperature in the middle of the barrel	240 – 250	°C
Front temperature of material barrel	250 – 260	°C
Mold temperature	60 – 90	°C
Melt Temperature	235 – 260	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.