| About |
|---|
| Product Description | |
|---|---|
| Supplier | DOMO |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Availabilitys | North America,Europe,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 10700 | MPa | ISO 527-2/1A |
| tensile strength | |||
| fracture | 189 | MPa | ISO 527-2/1A |
| Tensile strain | |||
| fracture | 3.3 | % | ISO 527-2/1A |
| Bending modulus | 9090 | MPa | ISO 178 |
| bending strength | 285 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 无断裂 | ISO 179-1eA | |
| Charpy Unnotch Impact strength | 无断裂 | ISO 179/1eU | |
| Impact strength of cantilever beam notch | 16 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | 无断裂 | ISO 180 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80.0 | °C | |
| Recommended maximum moisture content | 0.20 | % | |
| Temperature at the rear of the barrel | 225 to 230 | °C | |
| Temperature in the middle of the barrel | 230 to 240 | °C | |
| Front temperature of material barrel | 240 to 250 | °C | |
| Mold temperature | 80.0 to 100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |