| TECHNYL eXten® D 219WFC V50 Black is a polyamide 6.10, reinforced with 50% of glass fibre, heat stabilized with organic stabilizers, for injection moulding. This grade offers lower water uptake, higher dimensional stability and enhanced chlorine resistance versus standard PA 6.6. It offers too an enhanced corrosion resistance, a reduction in lead levels versus standard metal solutions and an increase in ease of processing and part design freedom versus metal solutions and other plastics. It is used for cold and warm water plumbing components including, but not limited to, components in contact with drinking water systems globally where elevated levels of chlorine could be present.&& |
| Product Description | |
|---|---|
| Supplier | DOMO |
| Generic | PA610 |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Food contact compliance,Good Dimensional Stability,HB,Low or no water absorption,Corrosion Resistant,Chlorine-resistant |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.50 | g/cm³ | ISO 1183/A |
| Water absorption rate | ISO 62 | ||
| 23℃，24hr | 0.24 | % | ISO 62 |
| Saturation, 23 ℃ | 2.0 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 16000 | MPa | ISO 527-2/1A |
| tensile strength | |||
| Fracture, 23 ℃ | 200 | MPa | ISO 527-2/1A |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.6 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 11800 | MPa | ASTM D790 |
| 23℃ | 12400 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 294 | MPa | ASTM D790 |
| 23℃ | 310 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 15 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 15 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 208 | ℃ | ISO 75-2/Af |
| Melting temperature | 225 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 6.1E+16 | ohms | IEC 60093 |
| Volume resistivity | 2.6E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 2 mm | 26 | kV/mm | IEC 60243-1 |
| Relative permittivity | 3.70 | IEC 60250 | |
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 | |
| Glowing wire flammability index | |||
| 1.6 mm | 700 | ℃ | IEC 60695-2-12 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 | °C | |
| Recommended maximum moisture content | 0.20 | % | |
| Temperature at the rear of the barrel | 270 to 280 | °C | |
| Temperature in the middle of the barrel | 275 to 285 | °C | |
| Front temperature of material barrel | 280 to 290 | °C | |
| Mold temperature | 70 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |