TECHNYL® ONE J 218 V35 NATURAL

About
TECHNYL® ONE J 218 V35 Natural is a polyamide, reinforced with 35% glass fiber reinforced, heat stabilized, for injection moulding. This product, based on a high fluidity matrix, offers strong benefits in term of productivity and excellent surface aspect. Due to significantly enhanced moisture resistance, it offers a higher dimensional stability than standard polyamide. This grade has high mechanical properties with excellent thermal behaviour. The results shown are based on an experimental grade. These results will be further enhanced and improved as more industrials lots are produced and statistical data are available.&&

About

TECHNYL® ONE J 218 V35 Natural is a polyamide, reinforced with 35% glass fiber reinforced, heat stabilized, for injection moulding. This product, based on a high fluidity matrix, offers strong benefits in term of productivity and excellent surface aspect. Due to significantly enhanced moisture resistance, it offers a higher dimensional stability than standard polyamide. This grade has high mechanical properties with excellent thermal behaviour. The results shown are based on an experimental grade. These results will be further enhanced and improved as more industrials lots are produced and statistical data are available.&&

Product Description
Supplier	DOMO
Generic	PA 66/6T
Material Status	Commercial: Active
Features	Good heat aging resistance,Good stripping performance,Good liquidity,Good surface appearance,Heat Stabilized,Good Dimensional Stability
Availabilitys	Africa & Middle East ,North America,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.44	g/cm³
Water absorption rate
23℃，24hr	0.65	%

MECHANICAL	Nominal value	Unit
Tensile modulus
23℃	11000	MPa
tensile strength
Fracture, 23 ℃	205	MPa
Tensile strain
Fracture, 23 ℃	2.5	%
Bending modulus	10000	MPa
bending strength	300	MPa

IMPACT	Nominal value	Unit
Charpy Notched Impact Strength
23℃	11	kJ/m²
Notched impact strength of cantilever beam
23℃	70	kJ/m²

THERMAL	Nominal value	Unit
Hot deformation temperature
1.8 MPa, unannealed	255	℃
Melting temperature	285	℃

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
0.80 mm	HB

Process Conditions
Injection	Nominal value	Unit	Test method
Injection instructions	Nominal value	Unit	Test method
drying temperature	80	°C
Recommended maximum moisture content	0.12	%
Temperature at the rear of the barrel	290 to 300	°C
Temperature in the middle of the barrel	295 to 305	°C
Front temperature of material barrel	300 to 310	°C
Mold temperature	90 to 110	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.